Nghĩa của từ paint film bằng Tiếng Việt

@Chuyên ngành kỹ thuật
-lớp sơn
@Lĩnh vực: xây dựng
-màng sơ

Đặt câu có từ "paint film"

Dưới đây là những mẫu câu có chứa từ "paint film", trong bộ từ điển Từ điển Anh - Việt. Chúng ta có thể tham khảo những mẫu câu này để đặt câu trong tình huống cần đặt câu với từ paint film, hoặc tham khảo ngữ cảnh sử dụng từ paint film trong bộ từ điển Từ điển Anh - Việt

1. ◦ Control A (surface application to cured alkyd paint film, 3648 ug/g ± 2%)

2. Bittiness paint defect in which paint film contains foreign matters like dust, grit, broken paint skin and fragments of bristle from brushes which project themselves out on the surfaces of the paint film

3. Brittleness describes the property of a coating or paint film that fractures when subjected to stress

4. The polyunsaturated fatty acid containing additives that lower trhe water resistance of the dry paint film.

5. The paint film thins from the effects of rain as it washes away the Chalking paint residue

6. Chalking: Formation of fine powder on the surface of the paint film during weathering which can cause color fading

7. Curtaining Gross sagging of a paint film, such that a pattern resembling the ruffles on a curtain is formed

8. The term 'Chalking' refers to the formation of a white, chalky powder on the surface of the paint film

9. DESCRIPTION The formation of fine, white powder on the surface of the paint film due to weathering, which may give the appearance of color fading. Although some degree of Chalking is normal and can be a desirable way for a paint film to wear, excessive paint …

10. Although some degree of Chalking is a normal, desirable way for a paint film to wear, excessive film erosion can result from heavy Chalking

11. Bridging is the covering of unfilled gaps, cracks or corner joints with a coating, which introduces a weakness in the paint film due to intermolecular and structural discontinuity

12. In order to shorten test time, a forced drying method is adopted in preparing sample so as to measure gloss and colour of self-curing paint film at ambient temperature.

13. Additionally, the polyunsaturated fatty acid moieties are capable of oxidative crosslinking during the curing process, forming a dry paint film that is more durable and water-resistant than traditional latex paint compositions.

14. To obtain elasticity imparting agents for paints comprised of liquid non-aqueous polymer dispersions which, when added to paints, improve the scratch resistance without lowering the acid resistance of the hardened paint film.